仕上げ時期が異なるコンクリート表層部の 走査型電子顕微鏡による硬化組織観察
https://iot.repo.nii.ac.jp/records/282
https://iot.repo.nii.ac.jp/records/28239f911ed-3126-4626-8594-c5ab33ba1607
| 名前 / ファイル | ライセンス | アクション |
|---|---|---|
仕上げ時期が異なるコンクリート表層部の 走査型電子顕微鏡による硬化組織観察 (2.8 MB)
|
.png)
|
| Item type | 紀要論文 / Departmental Bulletin Paper(1) | |||||
|---|---|---|---|---|---|---|
| 公開日 | 2023-03-08 | |||||
| タイトル | ||||||
| タイトル | 仕上げ時期が異なるコンクリート表層部の 走査型電子顕微鏡による硬化組織観察 | |||||
| タイトル | ||||||
| タイトル | Scanning Electron Microscope Observation of Hardened Concrete Surface at Different Finishing Time | |||||
| 言語 | en | |||||
| 言語 | ||||||
| 言語 | jpn | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | コンクリート床版 | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | 仕上げ | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | 査型電子顕微鏡 | |||||
| キーワード | ||||||
| 主題Scheme | Other | |||||
| 主題 | 反射電子像 | |||||
| キーワード | ||||||
| 言語 | en | |||||
| 主題Scheme | Other | |||||
| 主題 | Concrete Slab | |||||
| キーワード | ||||||
| 言語 | en | |||||
| 主題Scheme | Other | |||||
| 主題 | Finishing | |||||
| キーワード | ||||||
| 言語 | en | |||||
| 主題Scheme | Other | |||||
| 主題 | Scanning electron microscope | |||||
| キーワード | ||||||
| 言語 | en | |||||
| 主題Scheme | Other | |||||
| 主題 | Backscattered electron image | |||||
| 資源タイプ | ||||||
| 資源タイプ識別子 | http://purl.org/coar/resource_type/c_6501 | |||||
| 資源タイプ | departmental bulletin paper | |||||
| 著者 |
澤本, 武博
× 澤本, 武博× 沢木, 大介× 青山, 一真× 樋口, 正典× 臺, 哲義× SAWAMOTO, Takehiro× SAWAKI, Daisuke× AOYAMA, Masanori× HIGUCHI, Masanori× DAI, Akiyoshi |
|||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | 本研究では，仕上げ時期の異なるコンクリートの表面から深さ1.5mm程度の領域について，走査型電子顕微鏡による観察を行った．その結果，ブリーディング水が収まってから凝結始発時間までに仕上げると，表面の凹凸は小さく滑らかで，表層部に大きな気泡やひび割れは見受けられず，表層部の画像は明るく観察され，組織が緻密であることが分かった．しかし，比較的強度が高いコンクリートでは，凝結始発時間に仕上げると，表面の凹凸が大きくなり，表層部に大きな空隙も見受けられ，そこから生じたひび割れが観察された． | |||||
| 抄録 | ||||||
| 内容記述タイプ | Abstract | |||||
| 内容記述 | Although there have been many studies on the effect of concrete finishing time on surface quality, none have evaluated it through electron microscope imaging. The objective of this study is to visualize cross sections of the surface layers of concrete at different finishing times using electron microscopy imaging. For the first image, an area roughly 1.5 mm deep from the surface of the concrete was observed using a scanning electron microscope. When the concrete surface was finished and after the bleeding of water had stopped, the surface was smooth and no large voids or cracks were observed in the surface layer in the electron microscope image. In the image, the concrete surface layer was bright, and it was observed that the structure of the surface layer was dense. The second image is of high strength concrete. High strength concrete was difficult to finish at the initial setting time. Even after the bleeding of water had stopped, the surface of the concrete was hard, making the concrete difficult to finish. When finished at the initial setting time of the concrete, the surface was not smooth, and large voids and cracks were observed in the surface layer shown in the electron microscope image. | |||||
| 内容記述 | ||||||
| 内容記述タイプ | Other | |||||
| 内容記述 | 本研究では，仕上げ時期の異なるコンクリートの表層の状態を把握することを目的として，走査型電子顕微鏡（以下，SEMと称す）により表層部の断面を可視化し観察を行った． | |||||
| 書誌情報 |
ものつくり大学紀要 en : The Bulletin of Institute of Technologists 号 12, p. 5-12, 発行日 2023-03-08 |
|||||
| 出版者 | ||||||
| 出版者 | 学校法人ものつくり大学 | |||||
| 出版者 | ||||||
| 出版者 | Institute of Technologists | |||||
| ISSN | ||||||
| 収録物識別子タイプ | ISSN | |||||
| 収録物識別子 | 2185-3746 | |||||
| 関連サイト | ||||||
| 識別子タイプ | URI | |||||
| 関連識別子 | https://www.iot.ac.jp/ | |||||
| 関連名称 | ものつくり大学 | |||||