 note = {Effect of three curing temperatures and two periods after coating of both silane and silane-siloxane layers on the surface protection abilities of concrete was investigated. Three temperatures were 5°C, 20°C and 60°C. One period was three days at 5°C, 20°C and 60°C, respectively, then eleven days at 20°C. Another was fourteen days at 5°C, 20°C and 60°C, respectively. The higher the temperature was, the deeper a penetrating depth and the lower ratios of water permeability and chloride-ion penetration were. On the other hand, a ratio of water absorption was little decreased when the curing temperature was increased. As for the curing period, there was only a little difference between the two in the measurement. This means that the difference within three days at the beginning of the curing conditions effectively influenced the surface protection abilities., 本研究では，実際の現場施工で課題となる温度変化と，表面処理材塗布後の養生期間の違いが，表面保護効果に及ぼす影響について，実験的に検討する。
ここでは主として，JSCE-K571-2004⁴⁾に基づく表面保護効果の評価に加え，コンクリート表面の美観性に寄与する光沢度および表面色へ及ぼす影響についても併せて評価した結果を報告する。},
 pages = {69--75},
 title = {シラン系表面含浸材とシラン・シロキサン系表面塗布材の表面保護効果に及ぼす養生温度および養生期間の影響},
 year = {2013},